PA66(Polyamide (Nylon) 66) data sheet
--------------------------------------------------------------------------------
LEGEND
A = amorphous - Cr = crystalline - C = clear - E = excellent - G = good - P = poor
O = opaque - T = translucent- R = Rockwell - S = Shore
--------------------------------------------------------------------------------
STRUCTURE: Cr
SPECIFIC DENSITY: 1.14
WATER ABSORBTION RATE (%): 1.3
ELONGATION (%): 150
TENSILE STRENGTH (psi): 7600
COMPRESSION STRENGTH (psi): 8700
FLEXURAL STRENGTH (psi): 5800
FLEXURAL MODULUS (psi): 200000
IMPACT (IZOD ft. lbs/in): 2.1
HARDNESS: R100
FABRICATION
- BONDING: G
- ULTRASONIC WELDING: P
- MACHINING: G
DEFLECTION TEMPERATURE (deg. F)
- @ 66 psi: 390
- @ 264 psi: 250
UTILZATION TEMPERATURE (deg. F)
- min: -110
- max: 250
MELTING POINT (deg. F): 490
COEFFICIENT OF EXPANSION: 0.000044
ARC RESISTANCE: 130
DIELECTRIC STRENGTH (kV/mm): 18
TRANSPARENCY: T
UV RESISTANCE: G
CHEMICAL RESISTANCE
- ACIDS: P
- ALKALIS: P
- SOLVENTS: G
|